Surface Bioactivity of Sol Gel Derived 3Y-TZP Bioinert Ceramic through Hydroxylation Technique Using 5M H3PO4

R. Velmurugan, S. Kanagesan, S. Jesurani and T. Kalaivani

Abstract

Problem statement: This study presented bone like apatite formation on yttria stabilized zirconia in Simulated Body Fluid (SBF) through hydroxylation technique. Approach: Sol gel route was used to prepare yttria stabilized zirconia. Then it was hydroxylated with 5M H3PO4 for formation of Zr-OH group. Moreover, the growth rate of calcium and phosphate on zirconia substrate was examined using simulated body fluid. Results: From x-ray diffraction pattern, confirmed the phase formation of tetragonal zirconia. SEM analysis shows the growth of Ca-P on zirconia in SBF solution. AFM represents the particle size of Ca-P is about 68-70 nm for 7 days SBF and exactly 60 nm for 15 days SBF solution. Conclusion: The results showed that the yttria stabilized zirconia in SBF solution through hydroxylation gives better results.

American Journal of Applied Sciences
Volume 7 No. 3, 2010, 381-385

DOI: https://doi.org/10.3844/ajassp.2010.381.385

Submitted On: 20 February 2010 Published On: 31 March 2010

How to Cite: Velmurugan, R., Kanagesan, S., Jesurani, S. & Kalaivani, T. (2010). Surface Bioactivity of Sol Gel Derived 3Y-TZP Bioinert Ceramic through Hydroxylation Technique Using 5M H3PO4. American Journal of Applied Sciences, 7(3), 381-385. https://doi.org/10.3844/ajassp.2010.381.385